鋁卷廠家介紹鋁卷上色過程：
Aluminum coil manufacturers introduce the process of aluminum coil coloring
1、預(yù)處理,先運用方法對外表進行清洗,運用物理和化學(xué)方法都能夠,主要的就是使鋁卷.這樣是有利于氧化的完整的進行的,構(gòu)成的氧化膜也會是細密的.預(yù)處理還能夠運用一些機械設(shè)備處理.
1. Pretreatment, the use of methods to clean the external surface, the use of physical and chemical methods can, the most important is to make aluminum coil. This is conducive to the complete oxidation, the composition of the oxide film will be fine. Pretreatment can also use some mechanical equipment
2.陽極氧化,鋁卷廠家通過與處理之后的鋁卷,使基體發(fā)作陽極氧化反應(yīng),然后就是會生成細密的氧化薄膜.
2. Anodizing: aluminum coil manufacturers will react with the aluminum coil after treatment to form a fine oxide film

3.封孔,通過陽極氧化之后,氧化薄膜上會呈現(xiàn)許多的膜孔,封孔就是使這些膜孔關(guān)閉,防止氧化膜被污染.這種氧化膜是通明的,并且是具有吸附性的,這樣就會在孔內(nèi)堆積一些金屬鹽,這樣就能在外表顯顯露一些正本的銀白色,或者是之外的許多顏色.
3. Sealing, after anodizing, there will be many film holes on the oxide film. Sealing the hole is to close these film holes and prevent the oxide film from being polluted. This kind of oxide film is transparent and has adsorption, so some metal salts will be accumulated in the hole, so that some original silver white or many other colors can be displayed on the surface
鋁卷生產(chǎn)廠家
Aluminum coil manufacturer
鋁卷假設(shè)要投入運用，要在正常的溫度下，溫度不能過熱也不能太嚴寒，假設(shè)作為屋面，高度不得低于10度。在裝置之前，及時進行檢查，保證屋面的資料沒有磨損的表象，保證能夠正常的運用，在正常的情況下保證運用的壽命。鋁卷廠家螺栓頭要用防水性強的物質(zhì)密封，防止雨水進入生銹。
The aluminum coil is supposed to be put into use. The temperature should not be too hot or too cold under the normal temperature. It is assumed that as the roof, the height should not be less than 10 degrees. Before installation, timely inspection shall be carried out to ensure that there is no appearance of wear and tear on the roof data, so as to ensure normal operation and service life under normal conditions. The bolt head of aluminum coil manufacturer shall be sealed with waterproof material to prevent rainwater from entering and rusting.

鋁卷加工的環(huán)境溫度應(yīng)在7℃以上，要根據(jù)鋁卷厚度調(diào)整加工輥系的空隙，并鏟除輥面及托板上的異物;一起要檢查鋁卷雙面是不是脫漆，如脫漆，應(yīng)查明原因且采納辦法后才干繼續(xù)加工。
The ambient temperature of aluminum coil processing should be above 7 ℃. The gap of processing roller system should be adjusted according to the thickness of aluminum coil, and the foreign matters on the roller surface and support plate should be removed. It is necessary to check whether the paint on both sides of the aluminum coil is peeling off. If the paint is removed, the reason should be found out and the method should be adopted before continuing the processing.