鋁卷廠家發(fā)現(xiàn)在某些時(shí)候鋁卷的表面都會(huì)出現(xiàn)一些損傷，為了解決這一疑問(wèn)，我們特地的進(jìn)行了一番研究調(diào)查，找到了造成鋁卷表面出現(xiàn)損傷的幾個(gè)原因：
In order to solve this problem, we have carried out a special investigation and found out several reasons for the surface damage of aluminum coil
1、鋁卷廠家告訴大家因?yàn)樵谏a(chǎn)的時(shí)候有一些沉淀存在于鋁卷的表面，而且在處理的時(shí)候又未進(jìn)行均勻化處理或均勻化處理效果不好時(shí)，因此表面就殘留了一些金屬顆粒，因此在擠壓的過(guò)程中就會(huì)對(duì)鋁卷造成損傷；
1. The aluminum coil manufacturer tells us that because there are some precipitates on the surface of the aluminum coil during production, and when the homogenization treatment is not carried out or the homogenization treatment effect is not good, some metal particles are left on the surface, so the aluminum coil will be damaged in the extrusion process;

2、也有可能是有因?yàn)槟＞呱厦姹旧砭褪遣桓蓛舻模@樣在進(jìn)行工作的時(shí)候雜質(zhì)就會(huì)鋁卷造成劃傷，從而就造成了損傷的情況出現(xiàn)；
2. It is also possible that the mold itself is not clean, so impurities will scratch the aluminum coil when working, thus causing damage;
3、還有可能是以內(nèi)在從出料軌道上將其放到擺床過(guò)程中造成的，這是因?yàn)樵谶@個(gè)過(guò)程中是用叉料桿進(jìn)行運(yùn)輸?shù)?，很有可能就是在這個(gè)過(guò)程中造成的損傷。
3. It may also be caused in the process of placing it on the swing bed from the discharge track, because it is transported by fork bar in this process, which may be the damage caused in this process.
c告訴大家的這三點(diǎn)都是可能會(huì)造成鋁卷出現(xiàn)損傷的，當(dāng)然還會(huì)有一些其他的因素造成，如果大家比較感興趣，那么等到下次有機(jī)會(huì)的話，我們?cè)跒榇蠹依^續(xù)介紹吧。
Aluminum coil manufacturers tell you that these three points may cause aluminum coil damage, of course, there will be some other factors, if you are more interested, then wait until the next opportunity, we will continue to introduce it to you.